Tear-resistant paper. Ideal for tear-resistant hang tags and durable graphic applications in challenging full colour printing. Increased strength thanks to dimensionally stable and thermostable polyester film core.
ENDURO Premium 215 gloss 1s is a hard-wearing composite material consisting of a 36 µm PET film core and a white, gloss-coated paper surface on the front and natural uncoated paper on the back. The three-layer product structure is robust, resistant to edge tearing and water impermeable. It can be cut, punched, perforated, drilled, embossed, scored, folded, glued and bound without issue.
Both paper surfaces offer excellent printing results and great runnability and can be printed with all common standard inks and varnishes in offset and flexo printing. Suitable for laser printing and thermal transfer printing. With excellent colour rendering, high print contrast and good barcode readability, as well as perfect drying and ink/toner adhesion.
Thanks to the multi-layer product structure ENDURO offers an affordable, eco-friendly and sustainable alternative to fully synthetic media. It is PVC-free and FSC®-certified.
At a glance
- Increased tear resistance
- Water impermeable
- Excellent printability
NameWeight [g/m²]Value210Tolerance±15NormISO 536NameThickness (total) [µm]Value190Tolerance±15NormISO 534NameBending stiffness MD [mN]Value> 650ToleranceNormISO 2493-1; 15°/10mmNameBending stiffness CD [mN]Value> 300ToleranceNormISO 2493-1; 15°/10mmNameTensile strength MD [N/15mm]Value> 175ToleranceNormISO 1924-3/2/300NameTensile strength CD [N/15mm]Value> 110ToleranceNormISO 1924-3/2/300NameISO Brightness, front side [%]Value> 82ToleranceNormISO 2470-1NameISO Brightness, reverse side [%]Value> 82ToleranceNormISO 2470-1NameWhiteness, CIE, D65/10°, front sideValue> 100ToleranceNormISO 11475NameWhiteness, CIE, D65/10°, reverse sideValue> 110ToleranceNormISO 11475NameOpacity [%]Value> 94ToleranceNormISO 2471